Monitoring the damage of ductile cast iron by AE technique on fatigue loading発表情報:International Congress on Condition Monitoring and Diagnostic Engineering Management 2014 (COMADEM 2014), Brisbane, Australia ページ: 1-5キーワード:
AE technique; Non-destructive evaluation; Ductile cast iron; Crack initiation; Damage evaluation概要:抄録:Damage initiation and propagation characteristics of ductile cast iron due to crack, micro-crack have been investigated by acoustic emission (AE) technique. As spheroidal graphite cast iron has high strength as well as excellent workability and damping capacity, it has been widely used in automobile as well as in many other engineering applications. However, the damage initiation of the spheroidal graphite cast iron might depend not only on the graphite size but also on the distribution of the graphite nodules. The failures of this spheroidal graphite cast iron caused by cracks and micro-cracks have been investigated sequentially by AE technique. AE events during the initiation of cracks and micro-cracks have been characterized by comparing the microstructural images of the specimen. The result shows good acquisition performance in the evaluation process.英語フィールド
Author:Md. T. I. Khan, T. Nagao, S. Kitamura, K. Teramoto, N. Hattori, N. ShinoharaTitle:
Monitoring the damage of ductile cast iron by AE technique on fatigue loadingAnnouncement information:International Congress on Condition Monitoring and Diagnostic Engineering Management 2014 (COMADEM 2014), Brisbane, Australia Page: 1-5Keyword:
AE technique; Non-destructive evaluation; Ductile cast iron; Crack initiation; Damage evaluationAn abstract:Damage initiation and propagation characteristics of ductile cast iron due to crack, micro-crack have been investigated by acoustic emission (AE) technique. As spheroidal graphite cast iron has high strength as well as excellent workability and damping capacity, it has been widely used in automobile as well as in many other engineering applications. However, the damage initiation of the spheroidal graphite cast iron might depend not only on the graphite size but also on the distribution of the graphite nodules. The failures of this spheroidal graphite cast iron caused by cracks and micro-cracks have been investigated sequentially by AE technique. AE events during the initiation of cracks and micro-cracks have been characterized by comparing the microstructural images of the specimen. The result shows good acquisition performance in the evaluation process.